LNP™THERMOCOMP™ Compound 9X07430

SI

| British

| Metric

| PDF

Americas: COMMERCIAL

Also known as:LNP™Thermocomp™Compound 9X07430

Product reorder name:9X07430

PBT+PC Alloy, Glass and Mineral Filled, Opaque, Weatherable

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, yld, Type I, 5 mm/min	580	kgf/cm²	ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min	520	kgf/cm²	ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min	2.9	%	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	4.8	%	ASTM D 638
Tensile Modulus, 50 mm/min	33600	kgf/cm²	ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	1000	kgf/cm²	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	32000	kgf/cm²	ASTM D 790
Tensile Stress, yield, 5 mm/min	60	MPa	ISO 527
Tensile Stress, break, 5 mm/min	56	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	3.1	%	ISO 527
Tensile Strain, break, 5 mm/min	4.9	%	ISO 527
Tensile Modulus, 1 mm/min	3160	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	97	MPa	ISO 178
Flexural Modulus, 2 mm/min	3020	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	72	cm-kgf/cm	ASTM D 4812
Izod Impact, notched, 23°C	8	cm-kgf/cm	ASTM D 256
Instrumented Impact Energy @ peak, 23°C	91	cm-kgf	ASTM D 3763
Instrumented Impact Energy @ peak, -30	30	cm-kgf	ASTM D 3763
Multiaxial Impact	71	cm-kgf	ISO 6603
Instrumented Impact Total Energy, 23°C	142	cm-kgf	ASTM D 3763
Instrumented Impact Total Energy, -30°C	71	cm-kgf	ASTM D 3763
Izod Impact, unnotched 80*10*4 +23°C	47	kJ/m²	ISO 180/1U
Izod Impact, notched 80*10*4 +23°C	8	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT, 1.82 MPa, 3.2mm, unannealed	102	°C	ASTM D 648
CTE, -40°C to 40°C, flow	5.7E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow	8.3E-05	1/°C	ASTM E 831
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm	105	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Density	1.31	g/cm³	ASTM D 792
Moisture Absorption, 50% RH, 24 hrs	0.11	%	ASTM D 570
Mold Shrinkage, flow (5)	0.51	%	SABIC Method
Mold Shrinkage, xflow (5)	0.59	%	SABIC Method
Mold Shrinkage, flow, 24 hrs (5)	0.5 - 0.51	%	ASTM D 955
Mold Shrinkage, xflow, 24 hrs (5)	0.58 - 0.59	%	ASTM D 955
Density	1.31	g/cm³	ISO 1183
Moisture Absorption (23°C / 50% RH)	0.16	%	ISO 62

Source GMD, last updated:2011/01/20

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	80 - 110	°C
Drying Time	4 - 6	hrs
Drying Time (Cumulative)	24	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	260 - 280	°C
Nozzle Temperature	260 - 280	°C
Front - Zone 3 Temperature	260 - 280	°C
Middle - Zone 2 Temperature	255 - 275	°C
Rear - Zone 1 Temperature	245 - 270	°C
Mold Temperature	80 - 110	°C
Back Pressure	0.3 - 0.7	MPa